Scaling of the coercive field in ferroelectrics at the nanoscale. JETP Letters Volume 98, Issue 6, 2013, Pages 339-341
14 сентября 2018
231
| Предметная область | — |
| Выходные данные | — |
| Ключевые слова | — |
| Вид публикации | Статья |
| Контактные данные автора публикации | Gaynutdinov, R.a, Minnekaev, M.b, Mitko, S.c, Tolstikhina, A.a, Zenkevich, A.bd, Ducharme, S.e, Fridkin, V.a a Shubnikov Institute of Crystallography, Russian Academy of Sciences, Leninskii pr. 59, Moscow, 119333, Russian Federation b National |
| Ссылка на публикацию в интернете | www.scopus.com/ |
Аннотация
The scaling of the coercive field in ferroelectric films at the nanoscale is investigated experimentally. The scaling in the films of copolymer vinylidene fluoride and BaTiO3 with thickness equal by the order of value to the critical domain nucleus size 1-10 nm reveals deviation from the well-known Kay-Dunn law. At this thickness region coercive field does not depend on thickness and coincides with Landau-Ginzburg-Devonshire value.
Для того чтобы оставить комментарий необходимо авторизоваться.