Novel ternary compound Ce2RuAl: Synthesis, crystal structure, magnetic and electrical properties. Journal of Alloys and Compounds Volume 580, 2013, Pages 55-60
14 сентября 2018
224
| Предметная область | — |
| Выходные данные | — |
| Ключевые слова | — |
| Вид публикации | Статья |
| Контактные данные автора публикации | Murashova, E.a , Kurenbaeva, Z.a, Tursina, A.a, Marushina, E.a, Yaroslavtsev, A.b, Leshchev, D.b, Seropegin, Y.a, Kaczorowski, D.c a Department of Chemistry, Moscow State University, 119992 Moscow, Russian Federation b National Research Nuclea |
| Ссылка на публикацию в интернете | www.scopus.com |
Аннотация
The intermetallic phase Ce2RuAl was synthesized by arc melting the elemental components and subsequent annealing of the product at 823 K. Its crystal structure was determined from the single-crystal X-ray diffraction data and confirmed by powder X-ray diffraction at room temperature. The compound is of a new structural type related to the LaF3-type of structure: space group P63cm, Z = 6, a = 7.8362(7) Å, c = 9.7510(9) Å, Pearson symbol hP24. Some Ce-Ru distances in the unit cell are unusually short being equal to 2.4821(6) Å. This structural feature brings about instability in the cerium valence state, directly evidenced in the XANES data and corroborated in the study of bulk physical behavior in Ce2RuAl.
Indexed keywords
Elemental components; Intermetallic phase; Magnetic and electrical properties; Physical behaviors; Powder X ray diffraction; Single crystal x-ray diffraction; Structural feature; Ternary compounds
ПодробнееIndexed keywords
Elemental components; Intermetallic phase; Magnetic and electrical properties; Physical behaviors; Powder X ray diffraction; Single crystal x-ray diffraction; Structural feature; Ternary compounds
Для того чтобы оставить комментарий необходимо авторизоваться.