Intermetallic compounds Ce4Ru3Ga3 and La3Ru2Ga2 with crystal structures of new types. Journal of Alloys and Compounds Volume 575, 2013, Pages 183-189

14 сентября 2018
Предметная область
Выходные данные
Ключевые слова
Вид публикации Статья
Контактные данные автора публикации Shablinskaya, K.a , Murashova, E.a, Kurenbaeva, Z.a, Yaroslavtsev, A.b, Seropegin, Y.a, Kaczorowski, D.c a Department of Chemistry, Moscow State University, 119991 Moscow, Russian Federation b National Research Nuclear University MEPhI, 115409 M
Ссылка на публикацию в интернете AND PUB


Novel intermetallic phases Ce4Ru3Ga3 and La3Ru2Ga2 were synthesized by arc melting the elemental components. The Ce4Ru3Ga3 compound crystallizes with the orthorhombic unit cell of new structural type (space group Pnna, Z = 4) and the lattice parameters: a = 7.719(4) Å, b = 18.578(12) Å, c = 5.673(3) Å; while the La3Ru2Ga 2 compound has the monoclinic unit cell of new type (space group P21/m, Z = 6) and the lattice parameters: a = 5.8170(15) Å, b = 13.980(3) Å, c = 12.224(3) Å, b = 97.958(6)°. The characteristic feature of the Ce4Ru3Ga3 structure is very short distance of 2.7167 Å between one of the ruthenium atoms and one of the cerium atoms. This cerium atom adopts the intermediate valence state, which is reflected in the characteristic temperature dependence of the magnetic susceptibility of Ce4Ru3Ga3 and was directly confirmed by XANES spectroscopy. The latter experiment yielded the average valence of cerium ions near room temperature to be 3.19 ± 0.01. The compound exhibits metallic conductivity, fully consistent with its intermediate valence character.
Для того чтобы оставить комментарий необходимо авторизоваться.