Investigations of redistribution of iron in a zirconium alloy due to neutron irradiation . Hyperfine Interactions Volume 219, Issue 1-3, 2013, Pages 129-133
14 сентября 2018
240
| Предметная область | — |
| Выходные данные | — |
| Ключевые слова | — |
| Вид публикации | Статья |
| Контактные данные автора публикации | Filippov, V.P.a , Lauer, D.E.a, Lauer, Y.A.a, Petrov, V.I.a, Kargin, N.I.a, Permyakov, Y.V.b a National Research Nuclear University MEPhI, Moscow, Russian Federation b National Research Institute for Physic Technical and Radi |
| Ссылка на публикацию в интернете | www.scopus.com/record/display.url?origin=recordpage&eid=2-s2.0-84876183907&citeCnt=3&noHighlight=false&sort=plf-f&src=s&st1=MEPhI&nlo=&nlr=&nls=&sid=F0743CC1BB1CEC168410A18CB87C48A7.Vdktg6RVtMfaQJ4pNTCQ:6500&sot=b&sdt=b&sl=31&s=AFFIL(MEPhI) AND PU |
Аннотация
Data were obtained with the help of 57Fe Mössbauer spectroscopy about the redistribution of iron atoms between intermetallic precipitates and between precipitates and the solid solution phase in E635-type alloy (Zr-1. 2 wt% Sn-0. 34 wt% Fe-1. 0 wt %Nb-0. 03-0. 05 wt% O) due to neutron irradiation. © 2012 Springer Science Business Media Dordrecht.
--------------------------------------------------------------------------------
Author keywords
Mossbauer effect; Neutron irradiation; Zirconium alloys
--------------------------------------------------------------------------------
Author keywords
Mossbauer effect; Neutron irradiation; Zirconium alloys
Для того чтобы оставить комментарий необходимо авторизоваться.